Tailoring additive manufacturing to optimize dynamic properties in 316L stainless steel

Abstract

With the advent of additive manufacturing, manipulation of typical microstructural elements such as grain size, texture, and defect densities is now possible at a faster time scale. While the processing–structure–property relationship in additive manufactured metals has been well studied over the past decade, little work has been done in understanding how this process affects the dynamic behavior of materials. We postulate that additive manufacturing can be used to alter the material microstructure and used to enhance its dynamic strength. In this work, 316L stainless steel (SS) was manufactured via selected laser melting and its microstructure was altered through changing build parameters like laser power, speed, and hatch spacing systematically. These samples were then subjected to spall recovery experiments to measure the spall strength and quantify the amount of damage as a function of build parameters. By mapping the spall strength as a function of build parameters, this work demonstrated that indeed additive manufacturing can be used to tailor the spall strength of 316L SS. This work also determined the optimum build parameters (laser power=195W; scanning speed=1083mm/s; hatch spacing=0.09mm; layer thickness=0.02mm) to obtain the highest spall strength and the least amount of total damage in 316L SS. Microstructural characterization of the pre- and post-mortem samples revealed that increased grain average misorientation and textural index were the main driving force behind this higher spall strength. This work aims to enhance microstructural engineering techniques to design materials with greater resistance to dynamic shock loading.